Teak Deck Caulks Rated for Durability and Resistance to Chemicals

Teakdecking Systems teak caulk stands the test of time—and multiple chemical baths.

0

In June 2006, we began our test of seven caulks advertised for use in teak-deck seams. The goal was to evaluate each product on the four basic qualities anyone choosing a teak-deck caulk would want: ease of application, adhesion, durability, and resistance to chemicals.

The September 2006 issue reported on each product’s ease of application, and in the March 2007 issue, Practical Sailor rated the caulks on pliability, durability, and adhesion. In this update, we take a look at long-term durability and how each caulk reacts to multiple chemicals. Down the road, we’ll test the products’ strengths to failures and will rate the caulks’ overall performances, based on all of the previous tests.

What We Tested

Our caulk test group is a mix of polysulfide, polyether, silyl modified polyme

Teak Caulks

r (SMP), and silicone-based products, as well as both one- and two-part products that include three BoatLIFE caulks, Bostik/Simson Marine Special Range Deck Caulk Plus, MARITIME Teak Deck Caulk, Teakdecking Systems (TDS) SIS 440 Teak Deck Caulking, and West Marine’s Multi Caulk Sealant.

Noticeably absent are products from 3M and SIKA, both well known companies in the marine caulking arena that either do not have a product recommended for use on teak decks, or (in the case of SIKA) have one, but do not market it in the United States.

How We Tested

One of our primary goals was to see how well each caulk could hold up not only to the torture of ultraviolet (UV) rays, but to the chemicals that teak decks are likely to be exposed to during their lifetime. So, we applied a 4-inch bead of each test caulk to 16 different teak panels (8 inches by 4 inches), and then doused them regularly with the chemicals.

Thirteen of the panels were exposed to a single chemical; one was alternately exposed to each chemical; and another (our control panel) was exposed to no chemicals. Yet another—coated with a wood finish—was dropped from the test when it was obvious no chemicals were getting through the finish.

Teak Caulks

After a two-week curing period, all test panels were mounted outside, fully exposed to the weather, and given the initial chemical dose. Testers then applied the chemicals once a month for the following two years. The panels and each caulk bead were thoroughly saturated each time.

The chemical lineup included gasoline, diesel, motor oil, ammonia, household bleach, acetone, Star brite Teak brightener (oxalic acid), WD-40, brush cleaner, Fantastic multi-purpose cleaner, Murphy’s Oil soap, Methyl Ethyl Ketone (MEK), and a heavy-duty bilge cleaner from West Marine. The caulks seemed to have the hardest time with acetone and MEK.

Our test was admittedly harsh—it’s doubtful any teak deck has been tortured to the extent our test panels were. But it was intended to determine which caulks held up the best to chemicals.

A number of factors come into play when deciding just what makes a teak-deck caulk the easiest to apply. Everything else being equal (product quality, durability, etc.), ease of application to us means a quick curing, one-part caulk requiring no special cleaners or primers (both of which can add significantly to the job in terms of money and time). Spending $18 for a 6-ounce can of seam primer plus the additional step required to prime each seam—and waiting for the primer to dry before caulking—are good examples of things that impact application ratings.

Similarly, a caulk that can be sanded after 24 hours is preferable. We also consider one-part caulks to be less of a potential headache than two-part caulks. Even though you follow the directions for mixing to the letter, there’s always that nagging worry it won’t cure properly, or—horror of horrors—you somehow manage to tip over the can during mixing. (You were mixing it on the dock and not the deck, right?) One-part caulks come pre-mixed in nice, safe tubes or sausages, helping us protect ourselves from such self-inflicted woes.

For this evaluation, testers scratched, poked, and probed each caulk bead with their fingernails, and then ranked each on its pliability, texture, and overall physical condition for each chemical panel. A rating of Excellent indicates the caulk was still firm, supple, and in excellent condition. A rating of Fair indicates that the product was still in decent shape, but that testers were able make permanent indentions in the caulk with a thumb nail and were able to remove some of it by scratching along the length of the bead. A rating of Poor indicates that large chunks of the caulk were easily removed with a thumb nail and that overall, the caulk’s condition was clearly inferior.

What We Found

Teak Caulks

During our first caulk checkup (March 2007 issue), which was just eight months into our long-term evaluation, testers found that each of the seven products was holding its own with no signs of deterioration or damage. At that time, the softest caulk (West Marine Multi-Caulk) had the resilience of a neoprene wetsuit, while the hardest caulk (BoatLIFE Life Caulk) was slightly firmer than a pencil eraser.

However, now—two years after the application—testers found some eye-opening differences.

BoatLIFE Life-Caulk

Life-Caulk is a one-part, polysulfide-based rubber compound advertised for use above and below the waterline on fiberglass, wood, metal, and glass. It’s not recommended for use on plastics.

It was in the middle of the pack in our chemical test, earning good ratings on most panels, but only fair on the acetone, MEK, and WD-40 panels. The Life-Caulk beads on those panels hardened considerably, lost some adhesion, and were dry to the point that chunks of caulk were easily scratched off.

Bottom line: At $19, Life-Caulk Type P was one of the more expensive caulks tested. As for chemical resistance and longevity, Life-Caulk rated Fair overall and was not at the head of the class after two years.

BoatLIFE Teak Deck Sealant

Teak Deck Sealant is a one-part, silicone-based caulk advertised as resistant to teak cleaners, teak oils, gasoline, and diesel fuel. The Teak Deck Sealant test beads appeared in good shape, but all of them—including the control—were easily damaged with a tester’s thumb nail. Most of them maintained their elasticity, however, the bead on the All Chemicals panel lost adhesion, and testers were able to scratch chunks off the MEK victim with little effort.

Bottom line: BoatLIFE Teak Deck Sealant received a Poor in this durability test.

BoatLIFE Life-Caulk Type P

This product is a pourable, two-part polysulfide deck and hull seam compound advertised as resistant to teak cleaners, oils, fumes, gasoline, and diesel.

Testers found that the Life-Caulk Type P was holding up well after two years, rating Good on most chemical panels. The acetone bath did the most damage, however, the control panel bead still looked good—supple and not dried out like the BoatLIFE Deck Sealant.

Bottom line: The only two-part caulk tested, Life-Caulk Type P costs $68/qt and requires no special seam primers. It rated Fair overall in our chemical resistance/durability test. Performance-wise, it’s comparable to BoatLIFE Life-Caulk.

Bostik / Simson MSR Deck Caulk Plus

Teak Caulks

MSR Deck Caulk Plus is a one-part, silyl-modified, polymer-based caulk. According to the manufacturer, it is permanently elastic between -40°C to 100°C, and is extremely resistant to UV, temperature extremes, cleaners, and exposure to fresh and salt water. Our test beads of the MSR Deck Caulk Plus are still in excellent condition, maintaining pliability and adhesion.

Bottom line: MSR Deck Caulk Plus lives up to its claims and is impressive even after two years of chemical baths. It’s one of our three top picks so far. MSR’s downside is the need to prime each seam, and the cost of the special seam cleaner ($12 a pint) and primer ($40 a pint).

MARITIME Teak Deck Caulk

MARITIME Teak Deck Caulk is a one-part, “neutral curing, silicone adhesive sealant specially formulated for caulking teak decks” with “excellent temperature stability and resistance to chemicals and ultraviolet rays.”

Another top performer, the MARITIME test samples are still pliable and strong. All but one test bead received top ratings—the one that was doused with ammonia—and it still received a Good rating.

Bottom line: MARITIME Teak Deck Caulk is rated Excellent and is included in our top three picks.

Teakdecking Systems SIS 440

According to TDS’s literature, SIS 440 is a one-part, paste-like oxime cure system that forms a tough, flexible rubber compound; it does not sag during cure, and when cured, it has excellent temperature stability and chemical resistance. SIS 440 held up admirably to the onslaught of chemicals and cleaners. Testers gave it across-the-board Excellent ratings as it maintained adhesion and pliability without drying out or crumbling.

Bottom line: The TDS product showed Excellent chemical resistance and shows long-term durability at the two-year mark.

West Marine Multi-Caulk

Multi-Caulk Sealant is a polyether-based caulk billed as a versatile, waterproof sealant for use in teak-deck seams, bedding fittings, etc. It can be used above and below the waterline; with fiberglass, wood, glass, and metal; and claims to be unaffected by teak cleaners and brighteners, and oils and fuel.

Multi-Caulk received a mix of ratings, Good to Poor, in the chemical resistance test and had a particularly hard time with motor oil, MEK, Murphy’s oil, ammonia, and the Fantastic. Although the Multi-Caulk beads were still somewhat pliable, many were easily scratched by our tester’s thumbnail. The control panel Multi Caulk, with no chemical interaction, was rated Good.

Bottom line: The West Marine Multi-Caulk performed in the middle of the pack in this test.

Conclusion

Although the challenges of evaluating in two years a product that should last seven to 10 years are readily apparent, we were still able to make some hard and fast conclusions about the caulks and whether we would or would not use them on our own teak seams, particularly considering the time and effort involved in the re-caulking process.

Two silyl-modified polymers, Teakdecking Systems and Bostik/Simson MSR Deck Caulk Plus, along with the silicone-based MARITIME, are our top picks for chemical resistance and durability at two years. We gave the TDS caulk the edge due to its slightly better performance in chemical testing, and its better pricing and availability.

Darrell Nicholson
Practical Sailor has been independently testing and reporting on sailboats and sailing gear for more than 50 years. Supported entirely by subscribers, Practical Sailor accepts no advertising. Its independent tests are carried out by experienced sailors and marine industry professionals dedicated to providing objective evaluation and reporting about boats, gear, and the skills required to cross oceans. Practical Sailor is edited by Darrell Nicholson, a long-time liveaboard sailor and trans-Pacific cruiser who has been director of Belvoir Media Group's marine division since 2005. He holds a U.S. Coast Guard 100-ton Master license, has logged tens of thousands of miles in three oceans, and has skippered everything from pilot boats to day charter cats. His weekly blog Inside Practical Sailor offers an inside look at current research and gear tests at Practical Sailor, while his award-winning column,"Rhumb Lines," tracks boating trends and reflects upon the sailing life. He sails a Sparkman & Stephens-designed Yankee 30 out of St. Petersburg, Florida. You can reach him by email at practicalsailor@belvoir.com.